Certificates
| Characteristics | Norm | Symbol | Requirement |
|---|---|---|---|
| Pendulum Test | EN 15534-1:2014+A1:2017 Clause 6.4.2 & CEN/TS 15676:2007 | 55 | |
| Falling Mass Impact Resistance | EN 15534-1:2014+A1:2017 Clause 7.1.2.1 & EN 477:2018 | No cracks Maximum depth of residual indentation: 0.1mm |
|
| Breaking Load | EN 15534-1:2014+A1:2017 Clause 7.3.2 & Annex A | Front View 4278N Back View 4393N |
|
| Bending Strength | EN 15534-1:2014+A1:2017 Clause 7.3.2 & Annex A | Front View 33.8MPa Back View 34.3MPa |
|
| Modulus of Elasticity | EN 15534-1:2014+A1:2017 Clause 7.3.2 & Annex A | Front View 4280MPa Back View 4280MPa |
|
| Resistance to Indentation | EN 15534-1:2014+A1:2017 Clause 7.5 | Hardness Brinell: 71MPa Rate of Elastic Recovery: 71% |
|
| Creep Behavior | EN 15534-1:2014+A1:2017 Section 7.4.1 & EN 477:1995 | Deflection (ΔS): 2.522 mm Residual deflection (ΔSr): 1.615 mm |
|
| Flexural modulus-MOE | EN 15534-1:2014+A1:2017 Clause 7.3.2 & Annex A | Modulus of Elasticity: Front View 4280MPa Back View 4280MPa |
|
| Formaldehyde Emission | EN 717-1:2004 | ND (Not Detected) | |
| RoHS | IEC 62321-4:2013+Amd1:2017, IEC 62321-5:2013 & IEC 62321-7-2:2017 | ND (Not Detected) | |
| Fire Proof Test (Special formula) | GB/T 8626–2007, GB/T 20284–2006, GB8624–2012 | B1(C-s3, d1) | |
| Dimension Stability | GB/T24508–2009 | ≤ 0.5 mm | |
| Material Ageing of Chemical Industry | GB/T 16422.2–1999, GB/T250–2008 | Discoloration rating: 4 Class 1: sample completely changed Class 5: no change |
|
| Antimicrobial activity test | ASTM G21-15 | Rating: 0 (No growth on specimens after 28 days) | |
| Moisture Resistance (Boiling test) | EN 15534-1:2014+A1:2017 Clause 8.3.3 | 1.1% | |
| Creep Behavior | EN 15534-1:2014+A1:2017 Section 7.4.1 & EN 477:1995 | Deflection (ΔS): 2.522 mm Residual deflection (ΔSr): 1.615 mm |
|
| Resistance to Salt Spray | EN 15534-1:2014+A1:2017 Clause 8.6 & EN ISO 9227:2017 | No visible change Grade of chalking: 0 |
|
| Thermal Conductivity | EN 12664:2001 Heat flow meter method | 0.221 W/(m·K) | |
| Swelling and Water Absorption | EN 15534-1:2014+A1:2017 Clause 8.3.1 & EN 317:1993 | Water Absorption: 24h: 0.50%, 28d: 1.54% Swelling: See result |