Features
| Characteristics | Norm | Symbol | Requirement |
|---|---|---|---|
| Overall Thickness | ASTM F387 | 3.0 mm | |
| Wear layer | ASTM F410 20 | 22 mil or 0.55mm | |
| Dimension | ASTM F2055 |  |
7″ x 48″ Length: 0/+0.3 Width: 0/+0.4 |
| Beveled Edge |  |
Mircro Bevel | |
| Texture | Embossed / Wood Grain | ||
| Finish | UV Anti-Scratch Coating | ||
| Net Weight | 2.80 lbs/pcs, 39.28 lbs/box, 2171.55 lbs/pallet | ||
| Package | 14pcs/carton, 55cartons/pallet, 20pallets/container 20GP | ||
| Thickness toleranceUse | ISO24346 |  |
+0.13 /-0.10mm |
| Dimension tolerance (length/width) | ISO24342 | L：±0.50mm W：±0.15mm | |
| Dimensional Stability | ISO23999 | ≤0.10% | |
| Curling | ISO23999 | ≤1mm | |
| Squareness (plank) | ISO24342 | ≤0.20 | |
| Width Flatness | ISO10582 Annex B | Concave≤0.10%/Convex≤0.15% | |
| Length Flatness | ISO10582 Annex B | Concave≤0.50%/Convex≤1.0 % | |
| Openings / Assembling | ISO10582 Annex C | average≤0.15mm | |
| Ledging | ISO10582 Annex C | average≤0.10mm | |
| Chemical resistance | ASTM F925 | No change | |
| Surface treatment (UV) | base coating+top coating | ||
| Surface Integrity | ASTM F1914 | No puncture through wear layer into rigid core | |
| Residual Indentation | ASTM F1700/ASTM F1914 | ≤8% | |
| Castor Chair | ISO4918 |  |
25000R |
| Heat stability (color change) | ASTM F1514 | △E≤8 | |
| Light Stability (Color Change Test) | ASTM F1515 |  |
△E≤8 |
| Gloss Level | 4~6 | ||
| Reaction to Fire | ASTM E648 | ≥0.45W/cm² | |
| Optical smoke density | ASTM E662 | ≤450 | |
| Locking Strength | ISO10582 | N/A | |
| Resistance to Staining | EN423 | grade0 | |
| Micro Scratch Resistance | EN16094 |  |
≤grade2 |
| Abrasion Resistance (0.15/0.3/0.5MM) | ASTM D4060 |  |
1000R/2400R/4000R |
| Thermal Resistance | ASTM C518 |  |
0.02 to 0.05 m²·K/W (or 0.1 to 0.3 ft²·h·°F/BTU) |
| Slip Resistance (Slip Resistance for Coated Surfaces) | DN51130 |  |
R9 |
| Formaldehyde | ASTM E1333 | ≤ 0.041 ppm | |
| Heavy Metal content | ASTM F963 | Pb≤90ppm | |
| Pentachlorophenol (PCP) | CP 491510-01 | PCP levels ≤ 5 ppm | |
| Floor Heating System |  |
suitable | |
| FloorScore |  |
have | |
| TVOC | CA01350 | ≤0.5mg/m³ | |
| Flexibility | IS0 24344:2008，Method A | Test using a 20 mm mandrel. For products which show signs of cracking, perform a further test using a 50 mm mandrel. lf results show no further cracking,record the use of a 50 mm mandrel. |